Strength Characteristics on the Diffusion Bonded Joint of Intermetallic Compound TiAl and Structural Steel.

Sachio Seto, Koji Matsumoto, Tomomasa MASUYAMA, Misa HIROSHIMA, Hirotoshi Ishikawa

Abstract

In this research, diffusion bonding of the intermetallic compound TiAl containing Fe, V, B and SACM645 steel was investigated. Relationships between strength characteristics and bonding parameters were analyzed. Main results obtained are as follows, (1) Direct diffusion bonding of TiAl and SACM645 was possible, high strength joints were obtained by selecting short bonding time with the bonding temperature in the range of 1223-1283K.(2) In the bonding interface, two or three inter-layers were formed as diffusion process proceeded. Decarburized layer at the steel side, Fe-Al-Ti type layer and TiC layer at the TiAl side were formed.(3) High strength joints were obtained by suppressing the formation of TiC compound in the bonding interface and by controlling total width of inter-layers within 5μm.

Open-access reader

About this research paper

What this paper is about

Why it matters

OpenAlex reports 8 citations for this work. Citation counts describe recorded attention and do not establish research quality.

Key contribution

A contribution statement is not available in the OpenAlex record.

Method / approach

Method details are not available in the OpenAlex metadata.

Main findings

Findings are not separately available in the OpenAlex metadata.

Limitations

Limitations are not available in the OpenAlex metadata.

Applications

Application details are not available in the OpenAlex metadata.

Available abstract

Key concepts: Intermetallic, Diffusion bonding, Materials science, Bonding strength, Diffusion, Metallurgy, Layer (electronics), Joint (building)