High Temperature Performance of 316L-SS Joint Produced by Diffusion Bonding

Zi Liang An, Wei Ling Luan, Fu Zhen Xuan, Shan Tung Tu

Open full text 16 citations

Abstract

Two types of joining specimens with and without Ni foil interlayer between 316L–SS bar have been prepared by diffusion bonding in a temperature range of 850- 1050°C, under a uniaxial pressure of 10MPa for 1hours. The relationship between the bonding parameters and the tensile strength of the joints at elevated temperature was studied. Optimized processing parameters were suggested based on the testing results. It was found that the introduction of the interlayer may reduce the room temperature strength but increase the high temperature strength. This was attributed to the transformation of Fe0.64Ni0.36 formed in bonding process into FeNi3 at high temperature.

About this research paper

What this paper is about

Two types of joining specimens with and without Ni foil interlayer between 316L–SS bar have been prepared by diffusion bonding in a temperature range of 850- 1050°C, under a uniaxial pressure of 10MPa for 1hours. The relationship between the bonding parameters and the tensile strength of the joints at elevated temperature was studied. Optimized processing parameters were suggested based on the testing results. It was found that the introduction of the interlayer may reduce the room temperature strength but increase the high temperature strength. This was attributed to the transformation of Fe0.64Ni0.36 formed in bonding process into FeNi3 at high temperature.

Why it matters

OpenAlex reports 16 citations for this work. Citation counts describe recorded attention and do not establish research quality.

Key contribution

A contribution statement is not available in the OpenAlex record.

Method / approach

Method details are not available in the OpenAlex metadata.

Main findings

Findings are not separately available in the OpenAlex metadata.

Limitations

Limitations are not available in the OpenAlex metadata.

Applications

Application details are not available in the OpenAlex metadata.

Available abstract

Two types of joining specimens with and without Ni foil interlayer between 316L–SS bar have been prepared by diffusion bonding in a temperature range of 850- 1050°C, under a uniaxial pressure of 10MPa for 1hours. The relationship between the bonding parameters and the tensile strength of the joints at elevated temperature was studied. Optimized processing parameters were suggested based on the testing results. It was found that the introduction of the interlayer may reduce the room temperature strength but increase the high temperature strength. This was attributed to the transformation of Fe0.64Ni0.36 formed in bonding process into FeNi3 at high temperature.

Key concepts: Diffusion bonding, Materials science, FOIL method, Bonding strength, Atmospheric temperature range, Composite material, Ultimate tensile strength, Diffusion

Related papers

Related paper 1Related paper 2Related paper 3
Back to paper searchBrowse research topicsOriginal source
High Temperature Performance of 316L-SS Joint Produced by Diffusion Bonding — Research Paper | ScholarLens