Preliminary evaluation of a novel polyimide adhesive for bonding titanium and reinforced composites

A novel polyimide has been developed which shows promise as an adhesive for bonding titanium-to-titanium, titanium-to-polyimide composite and composite-to-composite with excellent lap shear strengths at room temperature and moderate strengths at 288 C. The adhesive is a high molecular weight polyimide made from commercially available monomers. The use of an ether as the solvent for the polymerization and for application of the polyamic acid enhanced the adhesive properties of the polyimide. At room temperature, P13N/glass composite bonded to titanium or to itself failed primarily in the surface layer of the composite, whereas at 260 C the failure was primarily cohesive. Failure of the P13N/unidirectional HT-S graphite composite-to-titanium bonded composites occurred in the composite regardless of the test temperature. Preliminary shear results with cross-plied P13N/HT-S graphite composite-to-composite specimens showed failure in the bonded surface fibers.