Solidification and transformation behaviour of austenitic stainless steel weld metals solidified as primary ferrite: Study of solidification and subsequent transformation of Cr-Ni stainless steel weld metals (2nd Report)

Summary Weld metals solidified in the ferritic-austenitic solidification mode (FA mode) have dual phases of ferrite and austenite in their as-solidified condition, where ferrite exhibits different morphologies depending on the chemical composition and welding conditions. This paper describes an investigation of the effect of the solidification and transformation sequence on the formation of final ferrite morphologies. Austenite is formed through either a eutectic reaction or peritectic reaction at the dendrite boundaries after the primary formation of ferrite. During the eutectic formation of austenite, the <100>δ direction of the primary ferrite and the <100>γ direction of the eutectic austenite are parallel to each other and lie along the growth direction of the primary dendrites. However, any specific lattice plane relationship between the two phases is not identified. During cooling after solidification, the austenite extends into the primary ferrite via solid-state transformation, and the final morphology of the ferrite is vermicular without any coherent orientation relationship between the primary ferrite and eutectic austenite. During peritectic formation of austenite, the Kurdjumov-Sachs orientation relationship is established between the primary ferrite and peritectic austenite, and the <100>γ direction of the peritectic austenite is not parallel to the growth direction of the primary dendrites. During cooling after solidification, the primary ferrite transforms into austenite, and the final morphology of the ferrite is lathy, since the primary ferrite and peritectic austenite have a favourable coherent orientation.