A Study of Rheological Behaviors of Al_2O_3-TiO _2 Slurry

Tao Ma

Open publisher page 0 citations

Abstract

The effect of mill time,dispersant content and solid volume fraction on rheological behaviors of Al_2O_3-TiO_2 slurry were investigated.The results showed that the viscosity of Al_2O_3-TiO_2 slurry was only 76 mPa·s and the solidification time was 360s after adding solidified agent when the mill time was 4h,the additive of dispersant was 3%(mass fraction of solid),and the solid volume content was 45%.And this slurry obtained the best fluid performance and abundant solidification time,was propitious to gelcasting.

About this research paper

What this paper is about

The effect of mill time,dispersant content and solid volume fraction on rheological behaviors of Al_2O_3-TiO_2 slurry were investigated.The results showed that the viscosity of Al_2O_3-TiO_2 slurry was only 76 mPa·s and the solidification time was 360s after adding solidified agent when the mill time was 4h,the additive of dispersant was 3%(mass fraction of solid),and the solid volume content was 45%.And this slurry obtained the best fluid performance and abundant solidification time,was propitious to gelcasting.

Why it matters

A significance statement is not available in the OpenAlex record.

Key contribution

A contribution statement is not available in the OpenAlex record.

Method / approach

Method details are not available in the OpenAlex metadata.

Main findings

Findings are not separately available in the OpenAlex metadata.

Limitations

Limitations are not available in the OpenAlex metadata.

Applications

Application details are not available in the OpenAlex metadata.

Available abstract

The effect of mill time,dispersant content and solid volume fraction on rheological behaviors of Al_2O_3-TiO_2 slurry were investigated.The results showed that the viscosity of Al_2O_3-TiO_2 slurry was only 76 mPa·s and the solidification time was 360s after adding solidified agent when the mill time was 4h,the additive of dispersant was 3%(mass fraction of solid),and the solid volume content was 45%.And this slurry obtained the best fluid performance and abundant solidification time,was propitious to gelcasting.

Key concepts: Dispersant, Slurry, Rheology, Mass fraction, Materials science, Volume fraction, Viscosity, Volume (thermodynamics)

Related papers

Related paper 1Related paper 2Related paper 3
Back to paper searchBrowse research topicsOriginal source
A Study of Rheological Behaviors of Al_2O_3-TiO _2 Slurry — Research Paper | ScholarLens