STRUCTURE AND CORROSION RESISTANCE OF ELECTROLESS PLATING Ni-P AND Ni-W-P COATINGS ON AZ91D MAGNESIUM ALLOY

Qin Gao-wu, Ren Yu-Beng, Fei Wen-Li, Duanyang Li, Bei Chen, Yang Zhong-dong

Open publisher page 1 citations

Abstract

Ni-P and Ni-W-P coatings were prepared on AZ91D magnesium alloy by a direct electroless plating processing.The microstructure,phases and corrosion resistance of the prepared and post-annealed coatings were studied by using scanning electron microscopy,X-ray diffraction technique and electrochemical test.The results show that the Ni-P coating is of amorphous structure while the Ni-W-P coating is of nanocrystalline structure with a grain size of about 7 nm,and they have similar corrosion resistance against 3.5%NaCl aqueous solution. The corrosion potential of the Ni-W-P coating after annealing at 250℃for 50 min positively shifts by 150 mV as compared to that of as-prepared Ni-W-P or Ni-P coating,implying the corrosion resistance of the annealed Ni-W-P coatings has been much improved.

About this research paper

What this paper is about

Ni-P and Ni-W-P coatings were prepared on AZ91D magnesium alloy by a direct electroless plating processing.The microstructure,phases and corrosion resistance of the prepared and post-annealed coatings were studied by using scanning electron microscopy,X-ray diffraction technique and electrochemical test.The results show that the Ni-P coating is of amorphous structure while the Ni-W-P coating is of nanocrystalline structure with a grain size of about 7 nm,and they have similar corrosion resistance against 3.5%NaCl aqueous solution. The corrosion potential of the Ni-W-P coating after annealing at 250℃for 50 min positively shifts by 150 mV as compared to that of as-prepared Ni-W-P or Ni-P coating,implying the corrosion resistance of the annealed Ni-W-P coatings has been much improved.

Why it matters

OpenAlex reports 1 citations for this work. Citation counts describe recorded attention and do not establish research quality.

Key contribution

A contribution statement is not available in the OpenAlex record.

Method / approach

Method details are not available in the OpenAlex metadata.

Main findings

Findings are not separately available in the OpenAlex metadata.

Limitations

Limitations are not available in the OpenAlex metadata.

Applications

Application details are not available in the OpenAlex metadata.

Available abstract

Ni-P and Ni-W-P coatings were prepared on AZ91D magnesium alloy by a direct electroless plating processing.The microstructure,phases and corrosion resistance of the prepared and post-annealed coatings were studied by using scanning electron microscopy,X-ray diffraction technique and electrochemical test.The results show that the Ni-P coating is of amorphous structure while the Ni-W-P coating is of nanocrystalline structure with a grain size of about 7 nm,and they have similar corrosion resistance against 3.5%NaCl aqueous solution. The corrosion potential of the Ni-W-P coating after annealing at 250℃for 50 min positively shifts by 150 mV as compared to that of as-prepared Ni-W-P or Ni-P coating,implying the corrosion resistance of the annealed Ni-W-P coatings has been much improved.

Key concepts: Materials science, Nanocrystalline material, Corrosion, Microstructure, Metallurgy, Coating, Magnesium alloy, Scanning electron microscope

Related papers

Related paper 1Related paper 2Related paper 3
Back to paper searchBrowse research topicsOriginal source
STRUCTURE AND CORROSION RESISTANCE OF ELECTROLESS PLATING Ni-P AND Ni-W-P COATINGS ON AZ91D MAGNESIUM ALLOY — Research Paper | ScholarLens