Microstructure and mechanical performance of brazed joints of Cf/SiC composite and Ti alloy using Ag–Cu–Ti–W

Cf/SiC composite was brazed to Ti alloy using interlayer of Ag–Cu–Ti–W mixed powder. The effects of W content and brazing parameters on the microstructure and properties of the brazed joints were investigated. The results show that W grains mainly distribute in Ag phase in the brazing layer and provide the effects of reinforcement and lowering residual thermal stress on the joint. The room temperature and 500°C shear strengths of the joints performed at 500°C for 30 min with Ag–Cu–Ti–50W (vol.-%) are remarkably higher than the optimal strengths of the joints brazed with Ag–Cu–Ti.