Processing and properties of solution impregnated carbon fiber reinforced polyethersulfone composites

Abstract Carbon fiber reinforced polymer composites are attractive because of their high stiffness and strength‐to‐weight ratios. In order to fully utilize the stiffness and strength of the reinforcement fiber, it is necessary to bring the polymer matrix and the reinforcement fiber together with homogeneous wetting. In this paper, a solution processing technique and the mechanical properties of carbon fiber reinforced polyethersulfone composites were investigated. The polymer was dissolved in cyclopentanone and fed onto a continuous carbon fiber tow using a drum winder. The solution‐processed composite prepregs were then layed up and compression molded into unidirectional composite panels for evaluation. The composite samples showed uniform fiber distribution and reasonably good wetting. The longitudinal flexural modulus was as high as 137 GPa, and longitudinal flexural strength 1400 MPa. In addition, the effects of polymer grade and processing conditions on the mechanical properties of the composites were discussed. It is suggested that the transverse properties and interlaminar fracture toughness could benefit from higher polymer matrix molecular weight. A careful design in the spatial distribution of the molecular weight would be necessary for practical applications.