Effect of Space Holder and Compaction Pressure on the Porosity of Sintered Copper

Shamsul Baharin Jamaludin, Chong Xin Yi, Alida Abdullah, Hussin Kamarudin

Open full text 2 citations

Abstract

The effect of space-holder content on the porosity of sintered copper that was fabricated by powder metallurgy technique has been investigated. Carbamide was used as space-holder and the content selected was 10 wt. %, 20 wt. % and 30 wt. %. A roll mill was used to mix the copper powder and the carbamide particles with rotation speed of 160 rpm for 2 hours. The mixture was compacted by hand press at 200-350MPa and sintered under argon atmosphere at 800°C. True density of the sample was determined by a gas pycnometer. Bulk density was determined using mass and volume of the sample. Result shows that the sintered porous copper with 30 wt. % of space-holder produced the highest porosity and the lowest density. Microstructure of pores was analyzed by a scanning electron microscope (SEM) which reveals the elongated pores interconnected to each other.

About this research paper

What this paper is about

The effect of space-holder content on the porosity of sintered copper that was fabricated by powder metallurgy technique has been investigated. Carbamide was used as space-holder and the content selected was 10 wt. %, 20 wt. % and 30 wt. %. A roll mill was used to mix the copper powder and the carbamide particles with rotation speed of 160 rpm for 2 hours. The mixture was compacted by hand press at 200-350MPa and sintered under argon atmosphere at 800°C. True density of the sample was determined by a gas pycnometer. Bulk density was determined using mass and volume of the sample. Result shows that the sintered porous copper with 30 wt. % of space-holder produced the highest porosity and the lowest density. Microstructure of pores was analyzed by a scanning electron microscope (SEM) which reveals the elongated pores interconnected to each other.

Why it matters

OpenAlex reports 2 citations for this work. Citation counts describe recorded attention and do not establish research quality.

Key contribution

A contribution statement is not available in the OpenAlex record.

Method / approach

Method details are not available in the OpenAlex metadata.

Main findings

Findings are not separately available in the OpenAlex metadata.

Limitations

Limitations are not available in the OpenAlex metadata.

Applications

Application details are not available in the OpenAlex metadata.

Available abstract

The effect of space-holder content on the porosity of sintered copper that was fabricated by powder metallurgy technique has been investigated. Carbamide was used as space-holder and the content selected was 10 wt. %, 20 wt. % and 30 wt. %. A roll mill was used to mix the copper powder and the carbamide particles with rotation speed of 160 rpm for 2 hours. The mixture was compacted by hand press at 200-350MPa and sintered under argon atmosphere at 800°C. True density of the sample was determined by a gas pycnometer. Bulk density was determined using mass and volume of the sample. Result shows that the sintered porous copper with 30 wt. % of space-holder produced the highest porosity and the lowest density. Microstructure of pores was analyzed by a scanning electron microscope (SEM) which reveals the elongated pores interconnected to each other.

Key concepts: Porosity, Materials science, Compaction, Copper, Scanning electron microscope, Powder metallurgy, Microstructure, Metallurgy

Related papers

Related paper 1Related paper 2Related paper 3
Back to paper searchBrowse research topicsOriginal source
Effect of Space Holder and Compaction Pressure on the Porosity of Sintered Copper — Research Paper | ScholarLens