EFFECT OF THERMOCYCLING ON BONDING OF COMPOSITE RESIN AFTER DENTIN SURFACE TREATMENTS

The purpose of this study was to evaluate the effect of various dentin surface treatments on shear bond strength, microhardness and fracture mode before and after thermocycling. Recently extracted 75 human molars were used. The teeth were sagittal sectioned faciolingually to obtain 150 specimens. They were randomly divided into six groups. Mesial and distal dentinal surfaces of specimens were exposed by grinding and treated respectively with GC-DENTIN CONDITIONER. 10-3 solution of 4-Meta, Cleansar and Primer of GLUMA, Scotchprep of Scotchbond 2, DENTIN CONDITIONER and PRIMER A, B of ALL BOND according to the manufacturers directions. Specimens of one group were not treated. Adhesive agent of Scotchbond 2, were applied and cured on the treated dentin surfaces. After P-50 were cured on them, specimens were stored in 31c water for 24 hours before shear bond strength measurement Shear bond strength was measured in 10 specimens of each group. 10 specimens of each group were thermocycled in , ,, , water in order, for 30 seconds respectively, 100 times a day for 7 days. After thermocycling shear bond strength was measured. Microhardness was checked on treated dentin surface and fractured dentin surface in 10 specimens respectievly. Francture modes were observed with SEM The following results were obtained. 1. Before thermocycling. shear bond strengths in the specimens treated with DENTIN CONDITIONER and PRIMER A, B of ALL BOND were significantly higher than those in other specimens(P