Dielectric Brekdown Chatacteristecs of the Gate Oxide for Ti-Polycide Gate

The degradation of dielectric breakdown field of 8nm-thick gate oxide () for Tipolycide MOS(meta1-oxide-semiconductor) capacitor with different annealing conditions and thickness of the polysilicon film on gate oxide was investigated. The degree of degradation in dielectric breakdown strength of the gate oxide for Ti-polycide gate became more severe with increasing annealing temperature and time, especially, for the case that thickness of the polysilicon film remained on the gate oxide after silicidation was reduced. The gate oxide degradation may be occurred by annealing although there is no direct contact of Ti-silicide with gate oxide. From SIMS analysis, it was confirmed that the degration of gate oxide during annealing was due to the diffusion of titanium atoms into the gate oxide film through polysilicon from the titanium silicide film.