Kinetic and Potential Sputtering Enhancements of Lunar Regolith Erosion: The Contribution of the Heavy Multicharged (Minority) Solar Wind Constituents

We report preliminary results for H+, Ar+1, Ar+6 and Ar+9 ion sputtering of JSC-1A lunar regolith simulant at solar wind velocities, obtain ed at the ORNL Multicharged Ion Research Facility using quadrupole ma ss spectrometry. The multi-charged Ar ions were used as proxies for i ntermediate mass solar wind multicharged ions. Prior to the Ar beam e xposures, the sample was exposed to high fluence H+ irradiation to si mulate H-loading due to the dominant solar wind constituent. A x80 en hancement of oxygen sputtering by Ar+ over same velocity H+ was measu red and an additional x2 increase for Ar+9 over same velocity Ar+ was demonstrated, giving clear evidence of the importance of potential s puttering by multicharged ions. This enhancement was observed to pers ist to the maximum fluences investigated (approx 10(exp 16)/sq cm). As discussed in a companion abstract by N. Barghouty, such persistent s puttering enhancement has significant implications on weathering and aging of lunar regolith. In addition, XPS measurements showed strong evidence of Fe reduction for those target areas that had been exposed to high fluence Ar+ and Ar+8 beams. Preferential oxidation of the Fe -reduced beam-exposed regions during transfer to the XPS system led t o enhanced O concentrations in those regions as well. On the basis of these very promising preliminary results, a NASA-LASER project on mo re extensive measurements was recently selected for funding. The prop osal expands the collaboration with NASA-MSFC for the simulation effort, and adds a new collaboration with NASA-GSFC for lunar mission-rele vant measurements.