Behavior of Damaged Graphite/Epoxy Laminates Under Compression Loading.

B. A. Byers

Abstract

The influence of three different resin systems on the damage tolerance of graphite/polymer laminates was evaluated. Testing consisted of both static compression and cyclic compression evaluation of 10.2 by 15.2 by 0.5 cm (4 by 6 by 0.2 in) laminates with circular holes, simulated delaminations, and low velocity impact. Damage growth under steadily increasing compression and cyclic compression loading was monitored. Damage size and impact-induced failures for the three materials were compared. Of the three material systems evaluated, the one most tolerant to impact damage exhibited the least delamination within the cross section due to impact, the highest transverse tension strain to failure, and the largest crack opening force, as determined from double cantilever beam tests.

About this research paper

What this paper is about

Why it matters

OpenAlex reports 54 citations for this work. Citation counts describe recorded attention and do not establish research quality.

Key contribution

A contribution statement is not available in the OpenAlex record.

Method / approach

Method details are not available in the OpenAlex metadata.

Main findings

Findings are not separately available in the OpenAlex metadata.

Limitations

Limitations are not available in the OpenAlex metadata.

Applications

Application details are not available in the OpenAlex metadata.

Available abstract

Key concepts: Materials science, Composite material, Epoxy, Compression (physics), Delamination (geology), Tension (geology), Composite laminates, Damage tolerance