Structure-Property Correlation of Hypoeutectic Al-7.6Si Alloys with and without Al-5Ti-1B Grain Refiner
Author information unavailable
Abstract
Author information unavailable
Abstract
Hypoeutectic Al-7.6Si alloy has been developed with and without Al-5Ti-1B grain refiner through the gravity casting method. Effects of 2, 4, and 6 wt % master alloy (Al-5Ti-1B) addition on the microstructural morphology, mechanical properties (percentage elongation (%El) and ultimate tensile strength (UTS)), hardness and fracture behaviour of the Al-7.6Si alloy have been investigated. Unmodified hypoeutectic Al-7.6Si alloy consists of needle and rod-like eutectic Si ((Si) E ) particles with sharp corners inside the Al α phase. In the grain refined Al-7.6Si alloy, TiB 2 is formed and these TiB 2 acts as a potential site for nucleation of Al α grains. Therefore, the grain refined alloys have fine globular Al α grains and fibrous (Si) E phase. The bulk hardness, UTS and elongation (%) are increased in the grain refined alloys. Further, fractography show that the cleavage fracture is reduced in the modified alloy and fine dimple formation is increased.
OpenAlex reports 8 citations for this work. Citation counts describe recorded attention and do not establish research quality.
A contribution statement is not available in the OpenAlex record.
Method details are not available in the OpenAlex metadata.
Findings are not separately available in the OpenAlex metadata.
Limitations are not available in the OpenAlex metadata.
Application details are not available in the OpenAlex metadata.
Hypoeutectic Al-7.6Si alloy has been developed with and without Al-5Ti-1B grain refiner through the gravity casting method. Effects of 2, 4, and 6 wt % master alloy (Al-5Ti-1B) addition on the microstructural morphology, mechanical properties (percentage elongation (%El) and ultimate tensile strength (UTS)), hardness and fracture behaviour of the Al-7.6Si alloy have been investigated. Unmodified hypoeutectic Al-7.6Si alloy consists of needle and rod-like eutectic Si ((Si) E ) particles with sharp corners inside the Al α phase. In the grain refined Al-7.6Si alloy, TiB 2 is formed and these TiB 2 acts as a potential site for nucleation of Al α grains. Therefore, the grain refined alloys have fine globular Al α grains and fibrous (Si) E phase. The bulk hardness, UTS and elongation (%) are increased in the grain refined alloys. Further, fractography show that the cleavage fracture is reduced in the modified alloy and fine dimple formation is increased.
Key concepts: Materials science, Alloy, Eutectic system, Ultimate tensile strength, Metallurgy, Nucleation, Elongation, Casting