Effects of Mn, Zn Additions and Cooling Rate on Mechanical and Corrosion Properties of Al-4.6Mg Casting Alloys

The mechanical properties of the Al-Mg alloy can be enhanced by adding metallic elements, but a continuous distribution of precipitates at grain boundaries leads to intergranular corrosion during sensitization treatment. In the present work, Mn, Zn additions, water cooling and furnace cooling were executed to investigate their effects on the mechanical and corrosion properties of the Al-4.6Mg alloy. Our results show that adding Mn to Al-4.6Mg alloys may produce grain refinement and dispersion strengthening, increasing tensile strength and hardness. The presence of Mn did not affect the corrosion resistance of Al-Mg alloys. Adding Zn to the Al-4.6Mg alloy increased tensile strength and hardness, but decreased corrosion resistance. Combined, the addition of Mn and Zn to the Al-4.6Mg alloy exhibited the highest tensile strength and hardness, but seriously reduced corrosion resistance. Furnace cooling substituted for water quenching could avoid intergranular corrosion, but slightly decreased the tensile strength and hardness by 7.0% and 6.8%, respectively.