Dynamics of Directed Self-Assembly of PS-b-PMMA during Solvent Annealing

Hiromichi Yamamoto

Open full text 0 citations

Abstract

The graphoepitaxy of symmetric PS-b-PMMA BCP film on the PS 60 mol% brush layer is carried out using the chemically homogeneous topological pattern of SiO2 layer and the home-made solvent annealing tool. It is confirmed by atomic force microscopy that PS-b-PMMA film on the periphery of the trench flows into the trench during the solvent annealing, so that the film thickness in the trench is thicker than that on the un-patterned area. The solvent annealing time dependence indicates the lamellar orientation in the trench changes from a mixture of the lamellar domain parallel and perpendicular to the side walls to the lamellar domain parallel to the side walls, and then changes back to the mixture, although the lamellar orientation perpendicular to the substrate remains the same. This result is also discussed with a free energy model for confined di-block copolymer. The lamellar domain parallel to the side walls indicates that the surface tensions of PS and PMMA blocks absorbing solvent vapor with the PS 60 mol% brush layer are not the same during the solvent annealing at 55 °C. Furthermore, the free energy difference between the parallel and perpendicular orientations is supposed to fluctuate due to the dynamics of PS-b-PMMA molecules by the solvent annealing, so that the lamellar orientation results in either of the lamellar domain parallel, perpendicular, or the mixture.

Open-access reader

About this research paper

What this paper is about

The graphoepitaxy of symmetric PS-b-PMMA BCP film on the PS 60 mol% brush layer is carried out using the chemically homogeneous topological pattern of SiO2 layer and the home-made solvent annealing tool. It is confirmed by atomic force microscopy that PS-b-PMMA film on the periphery of the trench flows into the trench during the solvent annealing, so that the film thickness in the trench is thicker than that on the un-patterned area. The solvent annealing time dependence indicates the lamellar orientation in the trench changes from a mixture of the lamellar domain parallel and perpendicular to the side walls to the lamellar domain parallel to the side walls, and then changes back to the mixture, although the lamellar orientation perpendicular to the substrate remains the same. This result is also discussed with a free energy model for confined di-block copolymer. The lamellar domain parallel to the side walls indicates that the surface tensions of PS and PMMA blocks absorbing solvent vapor with the PS 60 mol% brush layer are not the same during the solvent annealing at 55 °C. Furthermore, the free energy difference between the parallel and perpendicular orientations is supposed to fluctuate due to the dynamics of PS-b-PMMA molecules by the solvent annealing, so that the lamellar orientation results in either of the lamellar domain parallel, perpendicular, or the mixture.

Why it matters

A significance statement is not available in the OpenAlex record.

Key contribution

A contribution statement is not available in the OpenAlex record.

Method / approach

Method details are not available in the OpenAlex metadata.

Main findings

Findings are not separately available in the OpenAlex metadata.

Limitations

Limitations are not available in the OpenAlex metadata.

Applications

Application details are not available in the OpenAlex metadata.

Available abstract

The graphoepitaxy of symmetric PS-b-PMMA BCP film on the PS 60 mol% brush layer is carried out using the chemically homogeneous topological pattern of SiO2 layer and the home-made solvent annealing tool. It is confirmed by atomic force microscopy that PS-b-PMMA film on the periphery of the trench flows into the trench during the solvent annealing, so that the film thickness in the trench is thicker than that on the un-patterned area. The solvent annealing time dependence indicates the lamellar orientation in the trench changes from a mixture of the lamellar domain parallel and perpendicular to the side walls to the lamellar domain parallel to the side walls, and then changes back to the mixture, although the lamellar orientation perpendicular to the substrate remains the same. This result is also discussed with a free energy model for confined di-block copolymer. The lamellar domain parallel to the side walls indicates that the surface tensions of PS and PMMA blocks absorbing solvent vapor with the PS 60 mol% brush layer are not the same during the solvent annealing at 55 °C. Furthermore, the free energy difference between the parallel and perpendicular orientations is supposed to fluctuate due to the dynamics of PS-b-PMMA molecules by the solvent annealing, so that the lamellar orientation results in either of the lamellar domain parallel, perpendicular, or the mixture.

Key concepts: Annealing (glass), Solvent, Materials science, Chemistry, Organic chemistry, Composite material