Research on Anti-Corrosion Performance of Hot-dip Galvanized Coating during Neutral Salt Spray Test

D. Hu, Xiaoli Ma, Yaning Zhang

Open publisher page 1 citations

Abstract

Two customized hot-dip galvanized test specimens were applied onto the steel substrates, then the specimens were tested 5000h during the neutral salt spray and there were obvious differences in the anti-corrosion performance between the coatings. The results showed that there was no significant difference of the corrosion products and corrosion mechanisms between two coatings. Nevertheless, the Hot-dip customized production process, the density of the corrosion products in coating were the primary factors influencing the anti-corrosion performance of the Hot-dip galvanized coating.

About this research paper

What this paper is about

Two customized hot-dip galvanized test specimens were applied onto the steel substrates, then the specimens were tested 5000h during the neutral salt spray and there were obvious differences in the anti-corrosion performance between the coatings. The results showed that there was no significant difference of the corrosion products and corrosion mechanisms between two coatings. Nevertheless, the Hot-dip customized production process, the density of the corrosion products in coating were the primary factors influencing the anti-corrosion performance of the Hot-dip galvanized coating.

Why it matters

OpenAlex reports 1 citations for this work. Citation counts describe recorded attention and do not establish research quality.

Key contribution

A contribution statement is not available in the OpenAlex record.

Method / approach

Method details are not available in the OpenAlex metadata.

Main findings

Findings are not separately available in the OpenAlex metadata.

Limitations

Limitations are not available in the OpenAlex metadata.

Applications

Application details are not available in the OpenAlex metadata.

Available abstract

Two customized hot-dip galvanized test specimens were applied onto the steel substrates, then the specimens were tested 5000h during the neutral salt spray and there were obvious differences in the anti-corrosion performance between the coatings. The results showed that there was no significant difference of the corrosion products and corrosion mechanisms between two coatings. Nevertheless, the Hot-dip customized production process, the density of the corrosion products in coating were the primary factors influencing the anti-corrosion performance of the Hot-dip galvanized coating.

Key concepts: Galvanization, Corrosion, Salt spray test, Metallurgy, Coating, Materials science, Salt (chemistry), Dip-coating