Role of Bulky Retained Austenite in Austempered Ductile Iron

Chen Yang, Xi Xi Cui, Zhen Bo Zhao, Gao Hua, Cheng Liu

Open full text 4 citations

Abstract

In this investigation, the characteristics of bulky retained austenite in an austempered ductile iron are evaluated in two tempered conditions. which were intially tempered at 200oC for 1h before cooling to room temperature, and then tempered at 350oC for 1h. The result shows that the hardness within retained austenite areas is distributed unevenly with a range from 423 HV to 897 HV, which is attributed to the transformation from austenite to martensite during austempering. Also, the mechanism regarding the quenched marteniste formation is discussed. The poor fatigue resistance of ADI is hypothesized to be due to the amount of austenite transformed to martensite.

About this research paper

What this paper is about

In this investigation, the characteristics of bulky retained austenite in an austempered ductile iron are evaluated in two tempered conditions. which were intially tempered at 200oC for 1h before cooling to room temperature, and then tempered at 350oC for 1h. The result shows that the hardness within retained austenite areas is distributed unevenly with a range from 423 HV to 897 HV, which is attributed to the transformation from austenite to martensite during austempering. Also, the mechanism regarding the quenched marteniste formation is discussed. The poor fatigue resistance of ADI is hypothesized to be due to the amount of austenite transformed to martensite.

Why it matters

OpenAlex reports 4 citations for this work. Citation counts describe recorded attention and do not establish research quality.

Key contribution

A contribution statement is not available in the OpenAlex record.

Method / approach

Method details are not available in the OpenAlex metadata.

Main findings

Findings are not separately available in the OpenAlex metadata.

Limitations

Limitations are not available in the OpenAlex metadata.

Applications

Application details are not available in the OpenAlex metadata.

Available abstract

In this investigation, the characteristics of bulky retained austenite in an austempered ductile iron are evaluated in two tempered conditions. which were intially tempered at 200oC for 1h before cooling to room temperature, and then tempered at 350oC for 1h. The result shows that the hardness within retained austenite areas is distributed unevenly with a range from 423 HV to 897 HV, which is attributed to the transformation from austenite to martensite during austempering. Also, the mechanism regarding the quenched marteniste formation is discussed. The poor fatigue resistance of ADI is hypothesized to be due to the amount of austenite transformed to martensite.

Key concepts: Austempering, Austenite, Metallurgy, Materials science, Martensite, Cast iron, Wear resistance, Bainite

Related papers

Related paper 1Related paper 2Related paper 3
Back to paper searchBrowse research topicsOriginal source
Role of Bulky Retained Austenite in Austempered Ductile Iron — Research Paper | ScholarLens