Low Temperature Hot Corrosion Properties of NiAl-31Cr-3Mo Alloy

Jie Xing-di

Open publisher page 1 citations

Abstract

The low temperature hot corrosion behavior of NiAl-31Cr-3Mo alloy was investigated under constant temperature condition of 550 ℃,600 ℃,650 ℃ and 700 ℃.The microstructure of NiAl-31Cr-3Mo alloy before and after the low temperature hot corrosion were analyzed by means of optical microscopy(OM),SEM and TEM,and the mechanism of low temperature hot corrosion was discussed.There was an incubation period at the initial stage of hot corrosion.The continuous layers of Al2O3 and Cr2O3 were formed on the surface of NiAl-31Cr-3Mo alloy which provided protective effect at 550~650 ℃.At 650~700 ℃,the hot corrosion became serious,cavities were observed in the alloy surface,indicating pitting corrosion occurred,and the basic condition for the acid corrosion of Al-poor,Cr-poor and Mo-rich phases appeared.

About this research paper

What this paper is about

The low temperature hot corrosion behavior of NiAl-31Cr-3Mo alloy was investigated under constant temperature condition of 550 ℃,600 ℃,650 ℃ and 700 ℃.The microstructure of NiAl-31Cr-3Mo alloy before and after the low temperature hot corrosion were analyzed by means of optical microscopy(OM),SEM and TEM,and the mechanism of low temperature hot corrosion was discussed.There was an incubation period at the initial stage of hot corrosion.The continuous layers of Al2O3 and Cr2O3 were formed on the surface of NiAl-31Cr-3Mo alloy which provided protective effect at 550~650 ℃.At 650~700 ℃,the hot corrosion became serious,cavities were observed in the alloy surface,indicating pitting corrosion occurred,and the basic condition for the acid corrosion of Al-poor,Cr-poor and Mo-rich phases appeared.

Why it matters

OpenAlex reports 1 citations for this work. Citation counts describe recorded attention and do not establish research quality.

Key contribution

A contribution statement is not available in the OpenAlex record.

Method / approach

Method details are not available in the OpenAlex metadata.

Main findings

Findings are not separately available in the OpenAlex metadata.

Limitations

Limitations are not available in the OpenAlex metadata.

Applications

Application details are not available in the OpenAlex metadata.

Available abstract

The low temperature hot corrosion behavior of NiAl-31Cr-3Mo alloy was investigated under constant temperature condition of 550 ℃,600 ℃,650 ℃ and 700 ℃.The microstructure of NiAl-31Cr-3Mo alloy before and after the low temperature hot corrosion were analyzed by means of optical microscopy(OM),SEM and TEM,and the mechanism of low temperature hot corrosion was discussed.There was an incubation period at the initial stage of hot corrosion.The continuous layers of Al2O3 and Cr2O3 were formed on the surface of NiAl-31Cr-3Mo alloy which provided protective effect at 550~650 ℃.At 650~700 ℃,the hot corrosion became serious,cavities were observed in the alloy surface,indicating pitting corrosion occurred,and the basic condition for the acid corrosion of Al-poor,Cr-poor and Mo-rich phases appeared.

Key concepts: Nial, Corrosion, Materials science, Alloy, Metallurgy, Microstructure, Pitting corrosion, High-temperature corrosion

Related papers

Related paper 1Related paper 2Related paper 3
Back to paper searchBrowse research topicsOriginal source
Low Temperature Hot Corrosion Properties of NiAl-31Cr-3Mo Alloy — Research Paper | ScholarLens