2009•Physical Testing and Chemical AnalysisRequires access

Damage Cause Analysis of PD_3 Rail

Jianhui Deng

Open publisher page 0 citations

Abstract

After having been used four years in the curve sector R=600 m,some PD3 hot-rolled rails had fatigue damage of desquamation.The damage cause was analyzed by means of chemical composition analysis,mctallographic examination and hardness testing and so on.The result showed that the contact stress of rail and wheel being too excessive,the superficial metal of rail contact surface generated plastic deformation and forms fatigue crack,when the wearing speed rate was less than the fatigue crack expansion rate,the desquamation occured.And the measures were put forward.

About this research paper

What this paper is about

After having been used four years in the curve sector R=600 m,some PD3 hot-rolled rails had fatigue damage of desquamation.The damage cause was analyzed by means of chemical composition analysis,mctallographic examination and hardness testing and so on.The result showed that the contact stress of rail and wheel being too excessive,the superficial metal of rail contact surface generated plastic deformation and forms fatigue crack,when the wearing speed rate was less than the fatigue crack expansion rate,the desquamation occured.And the measures were put forward.

Why it matters

A significance statement is not available in the OpenAlex record.

Key contribution

A contribution statement is not available in the OpenAlex record.

Method / approach

Method details are not available in the OpenAlex metadata.

Main findings

Findings are not separately available in the OpenAlex metadata.

Limitations

Limitations are not available in the OpenAlex metadata.

Applications

Application details are not available in the OpenAlex metadata.

Available abstract

After having been used four years in the curve sector R=600 m,some PD3 hot-rolled rails had fatigue damage of desquamation.The damage cause was analyzed by means of chemical composition analysis,mctallographic examination and hardness testing and so on.The result showed that the contact stress of rail and wheel being too excessive,the superficial metal of rail contact surface generated plastic deformation and forms fatigue crack,when the wearing speed rate was less than the fatigue crack expansion rate,the desquamation occured.And the measures were put forward.

Key concepts: Desquamation, Materials science, Composite material, Deformation (meteorology), Metallurgy, Forensic engineering, Medicine, Engineering