Studies on the nature of multiple glass transitions in low acrylonitrile, butadiene–acrylonitrile rubbers

Abstract A study of the occurrence of multiple glass transitions in acrylonitrile–butadiene rubbers (NBR) has been made. Copolymerization theory was used to predict the change in comonomer composition with conversion for comonomer ratios both above and below the calculated azeotropic composition of 64% butadiene/36% acrylonitrile by weight. The results of these calculations suggested that multiple glass transitions, which occur only in NBR of less than 36% acrylonitrile, were due to an incompatibility of copolymer species of divergent comonomer compositions. This was shown by differential thermal analysis to be the case for various experimental polymers of known comonomer composition. A series of NBR's was prepared by incremental addition of acrylonitrile monomer during polymerization, and the resultant glass transition temperatures were evaluated. Results obtained showed that experimental samples which had single glass transitions also had a much narrower spread of comonomer species than the corresponding rubber polymerized with the use of full initial charge of both monomers. The data indicate that NBR's having a single glass transition, regardless of acrylonitrile content, may be prepared by incremental addition of acrylonitrile monomer during polymerization. Existing copolymerization theory appears to be adequate for predicting incremental monomer addition schedules suitable for the polymerization of NBR's having a single glass transition.