The annealing of damage in ion implanted gallium arsenide

Photoluminescence measurements at 77°K and Rutherford scattering of 450 keV protons were used to study radiation damage and annealing in ion implanted GaAs. The characteristic band edge luminescence (8225 Å) in GaAs is completely quenched by ion implantation. Photoluminescence measurements on samples which were isochronally annealed show a single annealing stage at 600°C. A luminescence peak at 9140 Å is introduced into the spectra of all implanted and annealed samples. This peak is attributed to an acceptor level created by As vacancies. The intensity of the peak is greatly reduced by protecting the surface of implanted layers with SiO2 during annealing. Rutherford scattering measurements on isochronally annealed samples reveal two annealing stages. A 300°C annealing stage is observed on samples which have an initial aligned yield less than random while a 650°C stage is observed on samples which have an initial aligned yield equal to random.