Stereoregularity of poly(methyl methacrylate) prepared by aqueous polymerization and catalyzed by corundum

Abstract The aqueous polymerization of methyl methacrylate was carried out in the absence and in presence of corundum or carborundum at 25 and 80°C. In the absence of corundum and carborundum, it has been found that rising the polymerization temperature from 25 to 80°C resulted in changing the tacticity of the obtained polymers. At 25°C the isotactic triad was 26% while the heterotactic triad was 33.5% and the syndiotactic one was 40.5%. Increasing the polymerization temperature to 80°C resulted in a decrease of the isotactic structure to 0% and increased the heterotactic structure and syndiotactic structure to 48 and 52% respectively. Polymerizing at 25°C in presence of corundum (0.5 g) an increase in the syndiotactic triad took place from 40.5 to 50.7% while the isotactic triad decreased from 26 to 22.2% and the heterotactic structure decreased from 33.5 to 27%. Raising the polymerization temperature to 80°C in the presence of the same amount of corundum resulted in an increase in both the isotactic and heterotactic triads to 35 and 32.7%, respectively. Polymerizing at 80°C in presence of corundum (0.5 g) resulted in nearly an equal percentage of each triad 33%.