Rheological, Mechanical and Morphological Properties of Poly(acrylonitrile-butadiene-styrene)/Polycarbonate Blends with ABS-g-MAH

Polymer blends containing poly(acrylonitrile-butadiene-styrene)(ABS) and polycarbonate (PC)(70/30, wt%) with compatibilizer were prepared using twin screw extruder. Compatibilizers were prepared by reactive extrusion with the ABS, maleic anhydride(MAH) and dicumyl peroxide(DCP) using twin screw extruder. In the ABS/PC (70/30) blends, tensile strength did not change significantly, but increased from 52.25 to 55.03 MPa when the ABS-g-MAH was added in the amount of 5 phr. From the results of rheological properties, storage modulus of the ABS/PC/ABS-g-MAH blends at low frequencies showed lager value than that of the ABS/PC(70/30) blend. From the results of the morphological properties of the ABS/PC(70/30) blend, it was observed that the drop size of the PC ranged from 1.2 to 1.5 μm and did not change significantly with the addition of the ABS-g-MAH(1~10 phr). From the results of the storage modulus, complex viscosity, and tensile strength of the ABS/PC (70/30) blends, it is found that the ABS-g-MAH is an effective compatibilizer in the ABS/PC (70/30) blends when the ABS-g-MAH is added in the amount of 5 phr.