EFFECT OF ANNEALING ON SHAPE MEMORY CHARACTERISTICS OF Ti -50.85at.% Ni ALLOY
Jong‐Il Kim, Tae-Hyeon Nam, Y. J. Lee, Shuichi Miyazaki
Abstract
Jong‐Il Kim, Tae-Hyeon Nam, Y. J. Lee, Shuichi Miyazaki
Abstract
In order to clarify the effect of annealing on the shape memory behavior of Ti -50.85at.% Ni alloy, the deformation and transformation behavior were investigated using tensile tests and differential scanning calorimeter (DSC). The martensitic transformation temperature increases with increasing annealing temperature until it reach as a maximum, and then decreases with further increasing annealing temperature. This can be rationalized by interaction between the distribution of Ti 3 Ni 4 precipitates and recovery of cold-worked structure. The R-phase transformation temperature increases with increasing annealing temperature until reaching a maximum, and then decreases with a further increase of annealing temperature. This is attributed to the change of Ni content in the matrix caused by precipitation of Ti 3 Ni 4. The critical stress for slip decreases rapidly with increasing annealing temperature, influenced by interaction between the distribution of Ti 3 Ni 4 precipitates and recovery of cold-worked structure.
OpenAlex reports 6 citations for this work. Citation counts describe recorded attention and do not establish research quality.
A contribution statement is not available in the OpenAlex record.
Method details are not available in the OpenAlex metadata.
Findings are not separately available in the OpenAlex metadata.
Limitations are not available in the OpenAlex metadata.
Application details are not available in the OpenAlex metadata.
In order to clarify the effect of annealing on the shape memory behavior of Ti -50.85at.% Ni alloy, the deformation and transformation behavior were investigated using tensile tests and differential scanning calorimeter (DSC). The martensitic transformation temperature increases with increasing annealing temperature until it reach as a maximum, and then decreases with further increasing annealing temperature. This can be rationalized by interaction between the distribution of Ti 3 Ni 4 precipitates and recovery of cold-worked structure. The R-phase transformation temperature increases with increasing annealing temperature until reaching a maximum, and then decreases with a further increase of annealing temperature. This is attributed to the change of Ni content in the matrix caused by precipitation of Ti 3 Ni 4. The critical stress for slip decreases rapidly with increasing annealing temperature, influenced by interaction between the distribution of Ti 3 Ni 4 precipitates and recovery of cold-worked structure.
Key concepts: Materials science, Annealing (glass), Shape-memory alloy, Alloy, Diffusionless transformation, Differential scanning calorimetry, Metallurgy, Martensite