Thermal studies of blends of poly(phenylene sulfide) (PPS) with poly(phenylene sulfide sulfone) (PPSS) and with poly(phenylene sulfide ether) (PPSE)

Abstract The miscibilities of poly(phenylene) sulfide/poly(phenylene sulfide sulfone) (PPS/PPSS) and poly(phenylene) sulfide/poly(phenylene sulfide ether) (PPS/PPSE) blends were invesigated in terms of shifts of glass transition temperatures Tg of pure PPS, PPSS, a dn PPSE. The crystallization kinetics of PPS/PPSS blends was also studied as a function of molar composition. The PPS/PPSS and PPS/PPSE blends are respectively partially and fully miscible. PPSE shows a plasticizing effect on PPS as does PPS on PPSS, which necessarily improves te processibility in the respective systems. We can control Tg and melting temperature Tm of PPS by varying amounts of PPSE in blends. The melt crystallization temperature Tmc of PPS/PPSE blends was higher than that of the PPSE homopolymer. Therefore, these blends require shorter cycle times in processing than pure PPSE. The overall rate of crystallization for PPS/PPSS blends follows the Avrami equation with an exponent ≃2. The maximal rate of crystallization for PPS/PPSS blends occurs at a temperatre higher by 10°C than that for PPS, while the crystallization half time t1/2 is 4 times shorter. In the cold crystallization range, crystal growth rates increase and Avrami exponents decrease significantly as the temperature increases.