Microstructure and Tensile Properties of a Mg-Zn-Y-Zr Alloy Containing Quasicrystal Phase Processed by Equal Channel Angular Pressing

Shi Wei Xu, Mingyi Y. Zheng, X.G. Qiao, Wei Min Gan, Kun Wu, S. Kamado, Yo Kojima

Open publisher page 3 citations

Abstract

Equal channel angular pressing (ECAP) was performed on extruded Mg-Zn-Y-Zr (Mg-5.0wt%Zn-0.9wt%Y-0.2wt%Zr) alloy at 300 oC. After 8 ECAP passes, average grain size of the alloy was reduced to about 1.4 μm, and the quasicrystalline phases were broken and dispersed in the matrix. In addition, nano- quasicrystallines were precipitated from the matrix during ECAP processing. After ECAP, the elongation to failure of the extruded material was significantly improved. Only after 2 ECAP passes, the elongation to failure was 29%, and after 8 ECAP passes, it reached 35%, which was three times larger than that of the as-extruded alloy. However, both yield strength and ultimate tensile strength were decreased with the increasing ECAP passes, which was considered to be resulted from the {0002} basal plane texture modification during ECAP.

About this research paper

What this paper is about

Equal channel angular pressing (ECAP) was performed on extruded Mg-Zn-Y-Zr (Mg-5.0wt%Zn-0.9wt%Y-0.2wt%Zr) alloy at 300 oC. After 8 ECAP passes, average grain size of the alloy was reduced to about 1.4 μm, and the quasicrystalline phases were broken and dispersed in the matrix. In addition, nano- quasicrystallines were precipitated from the matrix during ECAP processing. After ECAP, the elongation to failure of the extruded material was significantly improved. Only after 2 ECAP passes, the elongation to failure was 29%, and after 8 ECAP passes, it reached 35%, which was three times larger than that of the as-extruded alloy. However, both yield strength and ultimate tensile strength were decreased with the increasing ECAP passes, which was considered to be resulted from the {0002} basal plane texture modification during ECAP.

Why it matters

OpenAlex reports 3 citations for this work. Citation counts describe recorded attention and do not establish research quality.

Key contribution

A contribution statement is not available in the OpenAlex record.

Method / approach

Method details are not available in the OpenAlex metadata.

Main findings

Findings are not separately available in the OpenAlex metadata.

Limitations

Limitations are not available in the OpenAlex metadata.

Applications

Application details are not available in the OpenAlex metadata.

Available abstract

Equal channel angular pressing (ECAP) was performed on extruded Mg-Zn-Y-Zr (Mg-5.0wt%Zn-0.9wt%Y-0.2wt%Zr) alloy at 300 oC. After 8 ECAP passes, average grain size of the alloy was reduced to about 1.4 μm, and the quasicrystalline phases were broken and dispersed in the matrix. In addition, nano- quasicrystallines were precipitated from the matrix during ECAP processing. After ECAP, the elongation to failure of the extruded material was significantly improved. Only after 2 ECAP passes, the elongation to failure was 29%, and after 8 ECAP passes, it reached 35%, which was three times larger than that of the as-extruded alloy. However, both yield strength and ultimate tensile strength were decreased with the increasing ECAP passes, which was considered to be resulted from the {0002} basal plane texture modification during ECAP.

Key concepts: Materials science, Alloy, Ultimate tensile strength, Pressing, Elongation, Microstructure, Metallurgy, Quasicrystal

Related papers

Related paper 1Related paper 2Related paper 3
Back to paper searchBrowse research topicsOriginal source
Microstructure and Tensile Properties of a Mg-Zn-Y-Zr Alloy Containing Quasicrystal Phase Processed by Equal Channel Angular Pressing — Research Paper | ScholarLens