Microstructure and Mechanical Properties of Magnesium Alloy AZ81 with Yttrium

Qing Zhang, Quan An Li, Xiao Tian Jing, Xingyuan Zhang

Open full text 2 citations

Abstract

The effects of yttrium on the microstructure and mechanical properties of magnesium alloy AZ81 have been investigated by alloy preparation, microstructure analysis and tensile tests. The results show that proper content of yttrium addition can obviously refine the microstructure of magnesium alloy AZ81, reduce the amount of β-Mg17Al12 phase, lead to the precipitation of Al2Y phase and improve the mechanical properties. After solid solution and aging treatment, the tensile strength and elongation of the alloy increase at first and then decrease with the increase of yttrium content, and reach the maxima at 2%Y. At room temperature, the maxima are 277MPa and 10.9% respectively. At 150 , the maxima are 220MPa and 12.4% respectively.

About this research paper

What this paper is about

The effects of yttrium on the microstructure and mechanical properties of magnesium alloy AZ81 have been investigated by alloy preparation, microstructure analysis and tensile tests. The results show that proper content of yttrium addition can obviously refine the microstructure of magnesium alloy AZ81, reduce the amount of β-Mg17Al12 phase, lead to the precipitation of Al2Y phase and improve the mechanical properties. After solid solution and aging treatment, the tensile strength and elongation of the alloy increase at first and then decrease with the increase of yttrium content, and reach the maxima at 2%Y. At room temperature, the maxima are 277MPa and 10.9% respectively. At 150 , the maxima are 220MPa and 12.4% respectively.

Why it matters

OpenAlex reports 2 citations for this work. Citation counts describe recorded attention and do not establish research quality.

Key contribution

A contribution statement is not available in the OpenAlex record.

Method / approach

Method details are not available in the OpenAlex metadata.

Main findings

Findings are not separately available in the OpenAlex metadata.

Limitations

Limitations are not available in the OpenAlex metadata.

Applications

Application details are not available in the OpenAlex metadata.

Available abstract

The effects of yttrium on the microstructure and mechanical properties of magnesium alloy AZ81 have been investigated by alloy preparation, microstructure analysis and tensile tests. The results show that proper content of yttrium addition can obviously refine the microstructure of magnesium alloy AZ81, reduce the amount of β-Mg17Al12 phase, lead to the precipitation of Al2Y phase and improve the mechanical properties. After solid solution and aging treatment, the tensile strength and elongation of the alloy increase at first and then decrease with the increase of yttrium content, and reach the maxima at 2%Y. At room temperature, the maxima are 277MPa and 10.9% respectively. At 150 , the maxima are 220MPa and 12.4% respectively.

Key concepts: Microstructure, Yttrium, Materials science, Alloy, Ultimate tensile strength, Elongation, Metallurgy, Precipitation

Related papers

Related paper 1Related paper 2Related paper 3
Back to paper searchBrowse research topicsOriginal source
Microstructure and Mechanical Properties of Magnesium Alloy AZ81 with Yttrium — Research Paper | ScholarLens