First Performance Results of Ce:GAGG Scintillation Crystals With Silicon Photomultipliers

Jung‐Yeol Yeom, Seiichi Yamamoto, Stephen E. Derenzo, Virginia Spanoudaki, Kei Kamada, Takanori Endo, Craig S. Levin

Open publisher page 116 citations

Abstract

A new single-crystal Cerium doped Gd3Al2Ga3O123Al2Ga3O12(GAGG) scintillation crystal with high luminosity, high density and relatively fast decay time has successfully been grown. We report on the first performance results of the new GAGG scintillation crystal read out with silicon photomultipliers (SiPM) from Hamamatsu (MPPC) and FBK. The best energy resolution (511 keV peak of Ge-68) of 7.9% was attained with GAGG coupled to MPPC and 9.0% with the FBK SiPM after correcting for non-linearity. On the other hand, the best coincidence resolving time (FWHM) of polished 3 × 3 × 5 mm3and 3 × 3 × 20mm3crystals were 464 ±12 ps and 577 ±22 ps for GAGG crystals compared to 179 ±8 ps and 214 ±6 ps for LYSO crystals respectively with MPPCs. The rise time of GAGG was measured to be 200 ps (75%) and 6 ns (25%) while the decay time was 140 ns (92%), 500 ns (7.7%) 6000 ns (0.3%).

About this research paper

What this paper is about

A new single-crystal Cerium doped Gd3Al2Ga3O123Al2Ga3O12(GAGG) scintillation crystal with high luminosity, high density and relatively fast decay time has successfully been grown. We report on the first performance results of the new GAGG scintillation crystal read out with silicon photomultipliers (SiPM) from Hamamatsu (MPPC) and FBK. The best energy resolution (511 keV peak of Ge-68) of 7.9% was attained with GAGG coupled to MPPC and 9.0% with the FBK SiPM after correcting for non-linearity. On the other hand, the best coincidence resolving time (FWHM) of polished 3 × 3 × 5 mm3and 3 × 3 × 20mm3crystals were 464 ±12 ps and 577 ±22 ps for GAGG crystals compared to 179 ±8 ps and 214 ±6 ps for LYSO crystals respectively with MPPCs. The rise time of GAGG was measured to be 200 ps (75%) and 6 ns (25%) while the decay time was 140 ns (92%), 500 ns (7.7%) 6000 ns (0.3%).

Why it matters

OpenAlex reports 116 citations for this work. Citation counts describe recorded attention and do not establish research quality.

Key contribution

A contribution statement is not available in the OpenAlex record.

Method / approach

Method details are not available in the OpenAlex metadata.

Main findings

Findings are not separately available in the OpenAlex metadata.

Limitations

Limitations are not available in the OpenAlex metadata.

Applications

Application details are not available in the OpenAlex metadata.

Available abstract

A new single-crystal Cerium doped Gd3Al2Ga3O123Al2Ga3O12(GAGG) scintillation crystal with high luminosity, high density and relatively fast decay time has successfully been grown. We report on the first performance results of the new GAGG scintillation crystal read out with silicon photomultipliers (SiPM) from Hamamatsu (MPPC) and FBK. The best energy resolution (511 keV peak of Ge-68) of 7.9% was attained with GAGG coupled to MPPC and 9.0% with the FBK SiPM after correcting for non-linearity. On the other hand, the best coincidence resolving time (FWHM) of polished 3 × 3 × 5 mm3and 3 × 3 × 20mm3crystals were 464 ±12 ps and 577 ±22 ps for GAGG crystals compared to 179 ±8 ps and 214 ±6 ps for LYSO crystals respectively with MPPCs. The rise time of GAGG was measured to be 200 ps (75%) and 6 ns (25%) while the decay time was 140 ns (92%), 500 ns (7.7%) 6000 ns (0.3%).

Key concepts: Silicon photomultiplier, Physics, Crystal (programming language), Scintillation, Scintillator, Optics, Computer science, Detector

Related papers

Related paper 1Related paper 2Related paper 3
Back to paper searchBrowse research topicsOriginal source
First Performance Results of Ce:GAGG Scintillation Crystals With Silicon Photomultipliers — Research Paper | ScholarLens