Viscoplasticity of parylene-C film at body temperature
Jeffrey Chun-Hui Lin, Gilbert Lam, Yu‐Chong Tai
Abstract
Jeffrey Chun-Hui Lin, Gilbert Lam, Yu‐Chong Tai
Abstract
As parylene-C, a thermal plastic, has been extensively used as an implant material, its viscoplastic behavior at body temperature has never been systematically studied. Presented here is the first extensive in vitro study of the viscoplastic behaviors of 20-μm-thick parylene-C film at 37°C. The viscoplastic behaviors are investigated by uniaxial tensile tests at different strain rates (Figure 2), cyclic loading/unloading test (Figure 3) abrupt strain rate changing (Figure 4), creep-recovery (Figure 5), and stress-relaxation (Figure 6). There are three major conclusions here. First, below a stress of 2.5MPa, no observable viscoplastic behavior of 20-μm-thick parylene-C is found. Secondly, parylene-C film is a strain (or stress) and strain-rate dependent viscoplastic material. Thirdly, Burger's model is adequate to describe both creep and stress relaxation behaviors. In addition, the rate of the creep recovery (modeled with a single time constant) and stress relaxation (modeled with two time constants) decreases with increasing applied stress and/or strain.
OpenAlex reports 7 citations for this work. Citation counts describe recorded attention and do not establish research quality.
A contribution statement is not available in the OpenAlex record.
Method details are not available in the OpenAlex metadata.
Findings are not separately available in the OpenAlex metadata.
Limitations are not available in the OpenAlex metadata.
Application details are not available in the OpenAlex metadata.
As parylene-C, a thermal plastic, has been extensively used as an implant material, its viscoplastic behavior at body temperature has never been systematically studied. Presented here is the first extensive in vitro study of the viscoplastic behaviors of 20-μm-thick parylene-C film at 37°C. The viscoplastic behaviors are investigated by uniaxial tensile tests at different strain rates (Figure 2), cyclic loading/unloading test (Figure 3) abrupt strain rate changing (Figure 4), creep-recovery (Figure 5), and stress-relaxation (Figure 6). There are three major conclusions here. First, below a stress of 2.5MPa, no observable viscoplastic behavior of 20-μm-thick parylene-C is found. Secondly, parylene-C film is a strain (or stress) and strain-rate dependent viscoplastic material. Thirdly, Burger's model is adequate to describe both creep and stress relaxation behaviors. In addition, the rate of the creep recovery (modeled with a single time constant) and stress relaxation (modeled with two time constants) decreases with increasing applied stress and/or strain.
Key concepts: Viscoplasticity, Materials science, Creep, Stress relaxation, Composite material, Stress (linguistics), Strain rate, Relaxation (psychology)