Large deformation response of polycarbonate: Time‐temperature, time‐aging time, and time‐strain superposition

Paul A. O’Connell, Gregory B. McKenna

Open publisher page 186 citations

Abstract

Abstract Data are presented from tests of the stress relaxation response of a polycarbonate under torsional deformations. Tests were performed on samples over a range of strains from 0.0025 to 0.08, temperatures from 30 to 135°C and aging times from 1800 to 64,800 s. Individual data sets at each strain, temperature and aging time could be described using a stretched exponential form relaxation function, and time‐aging time superposition was found to be applicable to the data under all test conditions. The double logarithmic aging time shift rate, μ was found to vary significantly with both temperature and strain. Over the range of temperatures studied the data could be superimposed using conventional time‐temperature superposition. However, the master curve was found not to be described by a stretched exponential function. For strains up to 0.07, the data at each temperature could also be superimposed to form a master curve following the principle of time‐strain superposition. Interestingly, the master curves found from time‐strain and time‐temperature superposition did not have the same form. In both the time‐aging time and time‐temperature superposition analyses it was found that the application of vertical shifts was required for superposition of data.

About this research paper

What this paper is about

Abstract Data are presented from tests of the stress relaxation response of a polycarbonate under torsional deformations. Tests were performed on samples over a range of strains from 0.0025 to 0.08, temperatures from 30 to 135°C and aging times from 1800 to 64,800 s. Individual data sets at each strain, temperature and aging time could be described using a stretched exponential form relaxation function, and time‐aging time superposition was found to be applicable to the data under all test conditions. The double logarithmic aging time shift rate, μ was found to vary significantly with both temperature and strain. Over the range of temperatures studied the data could be superimposed using conventional time‐temperature superposition. However, the master curve was found not to be described by a stretched exponential function. For strains up to 0.07, the data at each temperature could also be superimposed to form a master curve following the principle of time‐strain superposition. Interestingly, the master curves found from time‐strain and time‐temperature superposition did not have the same form. In both the time‐aging time and time‐temperature superposition analyses it was found that the application of vertical shifts was required for superposition of data.

Why it matters

OpenAlex reports 186 citations for this work. Citation counts describe recorded attention and do not establish research quality.

Key contribution

A contribution statement is not available in the OpenAlex record.

Method / approach

Method details are not available in the OpenAlex metadata.

Main findings

Findings are not separately available in the OpenAlex metadata.

Limitations

Limitations are not available in the OpenAlex metadata.

Applications

Application details are not available in the OpenAlex metadata.

Available abstract

Abstract Data are presented from tests of the stress relaxation response of a polycarbonate under torsional deformations. Tests were performed on samples over a range of strains from 0.0025 to 0.08, temperatures from 30 to 135°C and aging times from 1800 to 64,800 s. Individual data sets at each strain, temperature and aging time could be described using a stretched exponential form relaxation function, and time‐aging time superposition was found to be applicable to the data under all test conditions. The double logarithmic aging time shift rate, μ was found to vary significantly with both temperature and strain. Over the range of temperatures studied the data could be superimposed using conventional time‐temperature superposition. However, the master curve was found not to be described by a stretched exponential function. For strains up to 0.07, the data at each temperature could also be superimposed to form a master curve following the principle of time‐strain superposition. Interestingly, the master curves found from time‐strain and time‐temperature superposition did not have the same form. In both the time‐aging time and time‐temperature superposition analyses it was found that the application of vertical shifts was required for superposition of data.

Key concepts: Superposition principle, Time–temperature superposition, Materials science, Polycarbonate, Logarithm, Relaxation (psychology), Strain (injury), Exponential function

Related papers

Back to paper searchBrowse research topicsOriginal source
Large deformation response of polycarbonate: Time‐temperature, time‐aging time, and time‐strain superposition — Research Paper | ScholarLens