Radiation‐induced emulsion copolymerization of tetrafluoroethylene with propylene. IV. Effects of emulsifier concentration and dose rate

Abstract Radiation‐induced emulsion copolymerization of tetrafluoroethylene with propylene was carried out by batch operation with an initial molar ratio of tetrafluoroethylene to propylene of 3.0 in the emulsifier concentration range of 0.1 to 3.0% and in the dose rate range of 2 × 104 to 2 × 105 R/hr. The effects of emulsifier concentration and dose rate on the polymerization rate and the number‐average degree of polymerization are discussed in comparison with the Smith‐Ewart theory. The polymerization rate is proportional to the 0.26 power of emulsifier concentration and to the 0.7 power of dose rate. The degree of polymerization is independent of the emulsifier concentration and the dose rate above the critical micelle concentration (CMC) of the emulsifier. These results are not in agreement with the Smith‐Ewart theory. It is explained that the termination reaction is a degradative chain transfer of propagating radicals to propylene. On the other hand, the copolymerization in emulsion occurs either below the CMC or in the absence of emulsifier. Under these conditions, however, it is impossible to obtain a copolymer of high molecular weight at a high rate of polymerization because of the presence of a small number of polymer particles formed and the short interval of chain growth in the polymer particle.