FTIR and DSC study of HDPE structural changes and mechanical properties variation when exposed to weathering aging during Canadian winter

P. Pag�s, F. Carrasco, Joan Saurina, Xavier Colom

Open publisher page 109 citations

Abstract

The aging of high-density polyethylene (HDPE) when exposed to drastic climatic conditions (Canadian winter, characterized by low temperature and abrupt temperature variations between the night and the day) was studied. The importance of degradation was determined by evaluating the microstructural changes in HDPE (i.e., oxidations, ramifications, and polymeric chain breaking) by means of FTIR spectrophotometry. The crystallinity variation in HDPE by FTIR and DSC was also studied. Both techniques led to coherent results: there was a loss of crystallinity due to weathering degradation. This crystallinity reduction produced a drastic decrease in impact energy. However, the other properties evaluated were not significantly affected. © 1996 John Wiley & Sons, Inc.

About this research paper

What this paper is about

The aging of high-density polyethylene (HDPE) when exposed to drastic climatic conditions (Canadian winter, characterized by low temperature and abrupt temperature variations between the night and the day) was studied. The importance of degradation was determined by evaluating the microstructural changes in HDPE (i.e., oxidations, ramifications, and polymeric chain breaking) by means of FTIR spectrophotometry. The crystallinity variation in HDPE by FTIR and DSC was also studied. Both techniques led to coherent results: there was a loss of crystallinity due to weathering degradation. This crystallinity reduction produced a drastic decrease in impact energy. However, the other properties evaluated were not significantly affected. © 1996 John Wiley & Sons, Inc.

Why it matters

OpenAlex reports 109 citations for this work. Citation counts describe recorded attention and do not establish research quality.

Key contribution

A contribution statement is not available in the OpenAlex record.

Method / approach

Method details are not available in the OpenAlex metadata.

Main findings

Findings are not separately available in the OpenAlex metadata.

Limitations

Limitations are not available in the OpenAlex metadata.

Applications

Application details are not available in the OpenAlex metadata.

Available abstract

The aging of high-density polyethylene (HDPE) when exposed to drastic climatic conditions (Canadian winter, characterized by low temperature and abrupt temperature variations between the night and the day) was studied. The importance of degradation was determined by evaluating the microstructural changes in HDPE (i.e., oxidations, ramifications, and polymeric chain breaking) by means of FTIR spectrophotometry. The crystallinity variation in HDPE by FTIR and DSC was also studied. Both techniques led to coherent results: there was a loss of crystallinity due to weathering degradation. This crystallinity reduction produced a drastic decrease in impact energy. However, the other properties evaluated were not significantly affected. © 1996 John Wiley & Sons, Inc.

Key concepts: Crystallinity, High-density polyethylene, Fourier transform infrared spectroscopy, Materials science, Weathering, Degradation (telecommunications), Polyethylene, Composite material

Related papers

Related paper 1Related paper 2Related paper 3
Back to paper searchBrowse research topicsOriginal source
FTIR and DSC study of HDPE structural changes and mechanical properties variation when exposed to weathering aging during Canadian winter — Research Paper | ScholarLens