Lubrication and failure mechanisms of graphite fluoride films

An optical microscope, equipped with a vertical illuminator and two polaroid filters (one rotatable), was used to visually study 440C HT steel surfaces lubricated with rubbed graphite fluoride films. Friction and wear results were compared to visual observations as a function of sliding distance for films applied to three surface finishes - polished, sanded, and sand-blasted. In general, the lubricating process was one of initial deformation or wear of metallic asperities into flat plateaus and then the formation of thin, layer-like, dynamic films which sheared between the flats and eventually flowed through the contact area. Failure was due to depletion of the graphite fluoride with the subsequent formation of excessive powdery metallic debris that formed a heavy, powdery film on both the rider and disk surfaces.