A Comparison of the Lubricating Mechanisms of Graphite Fluoride and Molybdenum Disulfide Films

Roberta Fusaro

Open full text 6 citations

Abstract

A microscopic study of 440C steel sliding surfaces lubricated by graphite fluoride or molybdenum disulfide solid lubricant rubbed films was conducted. The sliding surfaces, along with the friction, wear, and wear life were observed as a function of the number of sliding revolutions in three different atmospheres: moist air, dry air, or dry argon. In general, the lubricating mechanisms of the two solid lubricants were found to be relatively similar; that is, a dynamic, thin, layer-like film was formed between the two metallic surfaces. The mechanisms of failure were found to be somewhat different, however. Failure of MoS2 films was very dependent on atmospheric degradation, while that of graphite fluoride films was more dependent on flow of the lubricant film out of the contact zone.

Open-access reader

About this research paper

What this paper is about

A microscopic study of 440C steel sliding surfaces lubricated by graphite fluoride or molybdenum disulfide solid lubricant rubbed films was conducted. The sliding surfaces, along with the friction, wear, and wear life were observed as a function of the number of sliding revolutions in three different atmospheres: moist air, dry air, or dry argon. In general, the lubricating mechanisms of the two solid lubricants were found to be relatively similar; that is, a dynamic, thin, layer-like film was formed between the two metallic surfaces. The mechanisms of failure were found to be somewhat different, however. Failure of MoS2 films was very dependent on atmospheric degradation, while that of graphite fluoride films was more dependent on flow of the lubricant film out of the contact zone.

Why it matters

OpenAlex reports 6 citations for this work. Citation counts describe recorded attention and do not establish research quality.

Key contribution

A contribution statement is not available in the OpenAlex record.

Method / approach

Method details are not available in the OpenAlex metadata.

Main findings

Findings are not separately available in the OpenAlex metadata.

Limitations

Limitations are not available in the OpenAlex metadata.

Applications

Application details are not available in the OpenAlex metadata.

Available abstract

A microscopic study of 440C steel sliding surfaces lubricated by graphite fluoride or molybdenum disulfide solid lubricant rubbed films was conducted. The sliding surfaces, along with the friction, wear, and wear life were observed as a function of the number of sliding revolutions in three different atmospheres: moist air, dry air, or dry argon. In general, the lubricating mechanisms of the two solid lubricants were found to be relatively similar; that is, a dynamic, thin, layer-like film was formed between the two metallic surfaces. The mechanisms of failure were found to be somewhat different, however. Failure of MoS2 films was very dependent on atmospheric degradation, while that of graphite fluoride films was more dependent on flow of the lubricant film out of the contact zone.

Key concepts: Molybdenum disulfide, Dry lubricant, Lubricant, Graphite, Materials science, Molybdenum, Layer (electronics), Fluoride

Related papers

Related paper 1Related paper 2Related paper 3
Back to paper searchBrowse research topicsOriginal source
A Comparison of the Lubricating Mechanisms of Graphite Fluoride and Molybdenum Disulfide Films — Research Paper | ScholarLens